Specifications

• Material: Nickel Foam, Purity> 99.99% (excellent anti-corrosive)

  • Surface Density: 346g/m^2
  • Length:  200 mm  ± 0.5 mm
  • Width: 300mm ± 0.5 mm
  • Thickness: 1.6 mm ± 0.5 mm
  • Net weight: 21g
• Porosity: ≥95%   (80-110 Pores per Inch, average hole diameters about  0.25mm)
• Extensibility: Lengthwise≥5%;   Widthwise≥12%
• Tensile StrengthLengthwise≥1.25N/mm^2; Widthwise≥1.00N/mm^2:
• Young’s Modulus:   200 GPa
• Thermal Conductivity:  90.9 W/m·K
• Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of the nickel.
• How to clean the Nickel Foam for Battery Cathode Substrate.  

1. NiO can be removed by annealing in the hydrogen furnace.
2. Nickel foam (about 3.3 cm x 1 cm) was carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol were used for 5 min each to ensure the surface of the Ni foam was well cleaned. 

• MSDS DOWNLOAD

Porosity: ≥95%   (80-110 Pores per Inch, average hole diameter is about  0.25mm

Click the video above to see the battery cathode coated by MTI's Film coater MSK-AFA-II-VC

Other Metallic Foams

Related Product

Battery Powders

Heatable Ultrasonic Cleaner

Electrode Coating

Coin Cell Assembling

Pouch Cell Assembling

Cylinder Cell Assembling

Electrolyte injection