Die-60D is a Complete pressing die with 2 3/8" (60 mm) I.D. is ready for you to make 2" diameter sample pellet. The die is designed for our >30T Pressing machine
SPECIFICATIONS:
| Model |
Die-60D |
| Die Sleeve Height |
2 3/8" (60 mm) |
| Inside Diameter |
2 3/8" (60 mm) |
| Outside Diameter |
3 3/4" (101mm) |
Whole set pressing die includes |
- One 60mm I.D. core die made of hardened steel and highly polished with hardness HRC 60 - 62
- Ra 0.08μm highly polished steel
- One stainless steel sleeve is in outside to protect the die from cracking
- Two pushing rods highly polished and perfectly fitted into die
- Two steel support plates
- One steel cylinder for releasing out the sample.
- Max. Load: 150 metric Ton (at room temperature), or 500 MPa equivalent
- Max. working temperature 150oC
|
Pressing die installation schematic |
|
| Cautions |
- Please must always wear protective goggles during operation !!!
-
The pressing die cannot be used for pressing powder with particle size < 30 micron. Small particles may slip into the gap between the pushing rod and steel sleeve and cause damages to the sleeve during the compression. Ball mill and sieve the powder and apply only the 32~75 microns powder to the pressing die to avoid the damages. Please consider using the 3'' Dia. Sieve Set No.200&450 Mesh to seperate the 32~75 microns particles from the powder clumps. Please clean the mould via ethanol after the completion of each experiment.
- Please use alcohol to clean the pressing die every time before use and store it in a dry place with antirust oil after operation to avoid rusting on the surface, because all pressing dies are made by high-stretched carbon steel for achieving high hardness to meet essential requirements of making ceramic or metal samples. Otherwise, the pressing surface could probably get scratched.
- To avoid damaging the die core and sleeve, we strongly recommend you use the professional labotory hydraulic pressers which ensure the most even pressing interface and uniform pressure force.
- For pressing sticky metal powders such as Al, Mg, Zn, it is necessary to use dry or alcohol-based tool lubricant to lubricate the die and sleeve set to reduce friction during the compression.
- Do not press flammable, explosive materials.
|
| Application Note |
- You may consider using BNMR for easy mold release. Please click the picture below to order.
-
|