1.6mm Thick Nickel Foam for Battery Cathode Substrate or Solid-State Electrolyte Support (L 1000 x W 300 mm)-bcnf-16m

Minimum Order: $20 (equipment), $100 (crystals)

564 in stock

$424.35 USD

Sale Email for Lead Time

SKU: : \bcnf-16m

Product variants

Quantity

View full details

Nickel Foam for Battery Cathode Substrate or Solid-State Electrolyte Support (1m length x 300mm width x 1.6mm thickness) EQ-bcnf-16m

Specifications

Material: Nickel Foam, (excellent anti-corrosive)
Purity: > 99.9 wt %
Impurity: C≤200S≤80Fe≤100Cu≤100Si≤50 ( ppm)
Surface Density:346 g/m^2
Length: 1meter
Width: 300mm
Thickness: 1.6 mm
Net weight: 104g
Porosity: ≥95% (80-110 Pores per Inch. average hole diameters about 0.25mm)
Extensibility: Lengthwise≥5%; Widthwise≥12%
Tensile Strength Lengthwise ≥1.25N/mm^2; Widthwise≥1.00N/mm^2
Sold in roll only
Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of nickel.
How to clean the Nickel Foam for Battery Cathode Substrate.

It can be removed the NiO by annealing in the hydrogen furnace.
Nickel foam (about 3.3 cm x 1 cm) was carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol was used for 5 min each to ensure the surface of the Ni foam was well cleaned.