LSAT (111) 5x5x0.5 mm Square Substrate, 1 side epi polished - LSATc050505S1
LSAT (111) 5x5x0.5 mm Square Substrate, 1 side epi polished - LSATc050505S1
Minimum Order: $20 (equipment), $100 (crystals)
Shipping and handling will be applied
130 in stock
SKU: : \LSATc050505S1
Couldn't load pickup availability
LSAT (LaAlO3)0.3(Sr2AlTaO6)0.7 is a newly developing, twin-free crystal with a perovskite structure. LSAT has an excellent lattice match with high-Tc superconductors and many oxide materials. LSAT has a lower melting point and can be grown by Czochralski technology at lower cost. Therefore, it is expected to replace LaAlO3 and SrTiO3 as a common single-crystal substrate for epitaxial oxide thin films used in magnetic, ferroelectric, and superconducting devices.
Substrate Specifications
- Size: 5 × 5 × 0.5 mm ±0.05 mm
- Orientation: <111> ±0.5°
- Polishing: One side polished
- Surface Roughness: CMP polished with minimal subsurface damage, Ra < 10 Å
- Package: Class 100 plastic bag packed under Class 1000 clean-room conditions
Typical Physical Properties
| Chemical Formula | (LaAlO3)0.3(Sr2AlTaO6)0.7 or (La0.18Sr0.82)(Al0.59Ta0.41)O3 |
| Crystal Structure | Cubic: a = 3.868 Å |
| Growth Method | Czochralski |
| Density | 6.74 g/cm3 |
| Melting Point | 1840°C |
| Thermal Expansion | 10 × 10-6/°C |
| Dielectric Constant | ~22 |
| Color and Appearance | Colorless to light brown depending on annealing conditions. No twins or domains are visible. |