Single Crystal Powder of LiNiCoMnO2 (Ni:Co:Mn=6:1:3, NCM613) Powder for Li-ion Battery Cathode, 200g/bottle - Lib-LNCM613-SC
Single Crystal Powder of LiNiCoMnO2 (Ni:Co:Mn=6:1:3, NCM613) Powder for Li-ion Battery Cathode, 200g/bottle - Lib-LNCM613-SC
Minimum Order: $20 (equipment), $100 (crystals)
24 in stock
Regular price
$389.60 USD
Regular price
Sale price
$389.60 USD
Unit price
per
SKU: : \Lib-LNCM613-SC
Couldn't load pickup availability
Single Crystal LiNiCoMnO2 (Lithium Nickel Manganese Cobalt Oxide, Ni:Co:Mn=6:1:3, NCM613) with an electro-chemo-mechanically compliant microstructures has attracted great attention in Li-ion battery for its superior electrochemical performance compared to the polycrystalline counterpart
Specification
| Properties | Item | Standard Value |
|
Chemical Composition |
Ni (mol%) | 60.0 |
| Co (mol%) | 10.0 | |
| Mn (mol%) | 30.0 | |
|
Size Distribution |
D10 (μm) | 1.8 |
| D50 (μm) | 3.5 | |
| D90 (μm) | 6.3 | |
| Specific Surface Area (m2/g) | 0.84 | |
| Tap Density (g/cm³) | 2.50 | |
| Moisture (ppm) | 219 | |
| pH | 11.56 | |
|
Electrochemical Properties |
First discharge specific capacity (2032 coin battery, 0.1C/0.1C, 2.8-4.25V, mAh/g) | 190.8 |
| First charge and discharge efficiency (%) | 87 | |
| Charge & Discharge Graph |
 |
|
|
Note |
|
|
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in the vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.
- The product is for research only, not supply for large quantities,