This electrode sheet is based on Aluminum foil coated by Lithium Nickel Cobalt Aluminum Oxide (NCA811) on double sides and can be used as the cathode of Li-Ion battery -- 5 sheets /bag

SPECIFICATIONS

• Material:  LiNiCoAlO2  （Ni:Co:Al = Ni:Co:Al=8.15:1.5:0.35)
• Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
• Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.  
• Double sides area density: 21 ± 0.40 mg/cm2
• Compaction density: 3.4 ± 0.1 g/cm3
• Coating Thickness: ~62 um
• Total Thickness: ~78 um
• Active Material Weight: 8.32 g
• Active Material Proportion in Powder: 94% 
• Specific Capacity: 190 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]

• Note:  The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.