GaN  Template on saphhire is made by a hydride vapor phase epitaxy (HVPE)-based method. During the HVPE process, HCl reacts with molten Ga to form GaCl, which in turn reacts with NH3 to form GaN. GaN template is a cost effective way to replace GaN single crystal substrate

Specifications

• Sizes 10mmx10mm x0.5mm 
• Substrate Sapphire,  Orientation C (0001) +/- 1.0 ^o
• Conduction Type: n-type,
• Resistivity < 0.5 Ohm-cm
• Front Surface Finish (Ga Face) As-grown
•  Back Surface Finish Sapphire as-received finish
•  Useable Surface Area >90% 
•  Edge Exclusion Area 1mm
•  Package Single Wafer Container
• GaN layer thickness   30 microns , (+/- 10%) with roughness: ~10 nm RMS as measured by the Wyko (white light interferometer) for 50 umx50 um area

Related data

• Please click here to see XRD Rocking curve of GaN template
• Please click here to see Dislocation vs Thickness of GaN template
• Please click here to see RMS of GaN template