• LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810
1 1

LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810

LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810

Low stock: 10 left

$398.00 USD
$398.00 USD
Sale Email for Lead Time

SKU: Lib-LNCA810
View full details
LiNiCoAlO2 (Lithium Nickel Cobalt Aluminum Oxide) powder for Li-ion power battery cathode  200g/bottle (Ni:Co:Al =8.15:1.5:0.35)

Specification
Item Description
Composition

Li (NiCoAl) O2                      Ni:Co:Al=8.15:1.5:0.35

 Li = (7.2 ± 0.4)%
Ni+Co+Al = (59.0 ± 1.0)%
D10 (μm) 7.3
D50 (μm) 13.6
D90 (μm) 26.8
Dmax (μm) 39.9
Moisture
 380
pH
 11.7
Li2CO3 (%) 0.32
LiOH (%) 0.11
Fe (ppm) ≤100 ppm
Na (ppm) ≤200 ppm
Cu (ppm) ≤20 ppm



Specific Surface Area (m2/g) 0.5 BET Analyzer
Tapped Density (g/cm3) 2.40
Discharge Capacity (3.0-4.3V) (mAh/g) 195.7 @ 0.1C
Discharge Rate (%) 90.0 @2C vs.0.2C
Capacity Retention (RT, 3.0-4.3V, 1C/1C) (%) 92.3  1C@51cls
Optional You may order precursor to may your own composition ( click below link to order:
NiCoAl Precursor Powder (Ni0.8Co0.15Al0.05OH2 ) for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA


Application Notes:
  1. Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
  2. Please keep the powder in vacuum box to avoid moisture.
  3. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.
  4. This product is not manufactured by MTI.  We only sell small quantity to help the researcher developing new battery. If you have any question on IP conflict, let us know. We will forward the question to the manufacturer. 

Related Products

Vacuum Storage Box		 laboratory mill and mixer    
Powder Milling & Mixer 		 
Electrode Coaters
Battery Research Equipment
Other Battery Powders
Solid Electrolyte
×

Manufacturer Part Number: