Precursor Powder of NCMOH622 for High Capacity NCM Cathode Powder 200g/bottle - Lib-PNCM622
Precursor Powder of NCMOH622 for High Capacity NCM Cathode Powder 200g/bottle - Lib-PNCM622
Minimum Order: $20 (equipment), $100 (crystals)
Out of stock
SKU: : \Lib-PNCM622
Couldn't load pickup availability
There are 200 grams in one bottle
Note: You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use
Specification | |||
Package |
200g/bottle in a vacuumed bag |
||
Composition |
NCMOH622 (Ni:Co:Mn = 6.503 : 1.569: 1.928) |
||
Configuration |
Sphere |
||
Particle size distribution |
D104.33 μm |
||
Specific surface area |
4.09 m^2/g |
||
Tap Density |
≥1.64 g/cm^3 |
||
Water Content |
wt%0.36 |
||
PPH value |
~ 8.05 |
||
|
Main Element |
Required Content (mol) |
Ratio (Ni:Co:Mn) |
|
Li |
0 |
0 |
|
Ni |
40.0528 |
6.503 |
|
Co |
9.6601 |
1.569 |
|
Mn |
11.8743 |
1.928 |
|
Impurity |
Requiredppm |
Typicalppm |
|
Ca |
300 |
18 |
|
Cu |
50 |
8 |
|
Fe |
100 |
18 |
|
Mg |
300 |
19 |
|
Na |
500 |
232 |
|
Zn |
100 |
102 |
|
SO4 |
5000 |
3300 |
Note |
MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have a question for IP, we will forward your inquiry to the producer. |
||
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in a vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.