Precursor Powder of (Ni0.8Co0.15Al0.05(OH)2 for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA
Precursor Powder of (Ni0.8Co0.15Al0.05(OH)2 for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA
Low stock: 3 left
SKU: : \Lib-PNCA
Couldn't load pickup availability
EQ-Lib-Pre-NCA is the precursor of NCA (Ni0.8Co0.15Al0.05 (OH)2) for DIY Li--NCA cathode powder for high capacity Li-Ion cathode at your own composition.
Note: You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use
Specification
|
Package |
200g/bottle in a vacuumed bag |
||
|
Composition |
Ni0.8Co0.15Al0.05OH2 |
||
|
Configuration |
Sphere |
||
|
Particle size distribution |
D105±0.5μm |
||
|
Specific surface area |
~1.5m2/g |
||
|
Tap Density |
≥1.8g/cm3 |
||
|
Water Content |
500ppm |
||
|
PPH value |
≤11.2 |
||
|
Mian Element |
Required Content |
Real Content% |
|
|
Li |
0 |
0 |
|
|
Ni |
80±0.5 |
80.07 |
|
|
Co |
15±0.5 |
15.10 |
|
|
Al |
5±0.5 |
4.77 |
|
|
Impurity |
Requiredppm |
Typicalppm |
|
|
Ca |
300 |
49.58 |
|
|
Cu |
50 |
ND |
|
|
Fe |
100 |
96.34 |
|
|
Cr |
50 |
27.51 |
|
|
Mg |
300 |
44.56 |
|
|
Na |
500 |
119.85 |
|
|
S |
2000 |
391.5 |
|
|
Zn |
100 |
4.19 |
|
|
Mn |
100 |
29.98 |
|
|
Si |
300 |
75.23 |
|
|
Zr |
5000 |
390.0 |
|
|
Y |
250 |
170.12 |
|
|
Note |
MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have the question for IP, we will forward your inquiry to the producer.
|
||
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in a vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.