Hi-Pressure Super Alloy Tube with Flanges: OD 60x ID 52 x L1000 (mm), Max.100oC -TGH60D1000

Hi-Pressure Super Alloy Tube with Flanges: OD 60x ID 52 x L1000 (mm), Max.100oC -TGH60D1000

Out of stock

Price: RFQ

SKU: : \TGH60D1000

Choose your Variant:



View full details

Ni-based superalloy tube vessel (OD 60 x ID 52 x L 1000 (mm)). It can be used under ultra-highly oxidizing and inert gas atmospheres up to 1100°C to process special compounds. It is a consumable part of OTF-1200X-HPV, which is a compact HIP (hot isostatic pressure) furnace for researching the new generation of materials at low cost.

Specification:

    Outside Diameter:          60 mm
    Inside Diameter:           52 mm
    Tube Length:                             1000 mm
    Max. working temperature
    without load:  
         1100 °C
     Working Pressure
             &
    Temperature:
 
Maximum pressure inside the tube
Heating temperature
Max. 7Mpa <700C
Max. 580 PSI  (4Mpa)       (40 Bar) 800°C
Max. 362 PSI  (2.5 Mpa)   (25 Bar) 900°C
Max. 174 PSI  (1.2 Mpa)   (12 Bar) 1000°C
Max. 116 PSI  (0.8 Mpa)   (8 Bar) 1100°C (for <1hr)
Warning
  • Please set up a pressure alarm point in the digital pressure display before the operation
  • Must install a pressure regulator on the gas cylinder to increase pressure gradually.
  • Service-life design for 2,000 hours at 800oC. The high-pressure vessel is a consumable part, please order replacement once found the deformation
      Installation:
  •         
  • Adjustable High-Pressure Relief Valve is not included and available upon request.
     Optional
  • A high-temperature pressure transmitter, MTI-ZQ-GW is available upon request.
  •      
      Attention:
  • In order get longer tube service life, Please use quartz or alumina crucible to carry the sample, instead of loading sample directly inside the tube, please click the picture below to choose one crucible boat:
                                                                       